SIFAT MEKANIK DAN OPTIK KACA SENG MAGNESIUM FOSFAT

  • Eko Budiyanto Prodi Fisika FMIPA Universitas Negeri Jakarta, Jl. Rawamangun Muka No 1, Jakarta 13220
  • Agus Setyo Budi Prodi Fisika FMIPA Universitas Negeri Jakarta, Jl. Rawamangun Muka No 1, Jakarta 13220
  • Erfan Handoko Prodi Fisika FMIPA Universitas Negeri Jakarta, Jl. Rawamangun Muka No 1, Jakarta 13220
  • Md. Rahim Sahar Jabatan Fizik Fakulti Sains Universiti Teknologi Malaysia, UTM Skudai, Johor 81310

Abstract

Glass ZnO-MgO-P2O5 with the addition of ZnO composition between 0-15 mol% has been successfully using techniques Melt Quenching. With the analysis of X-ray diffraction (XRD) structure of glass obtained showed properties of amorphous materials. Photoluminescence spectrum has a dominant emission band on the observation of the peak at around 385nm. Sedangjkan hardness test of glass ZnO-MgO-P2O5 decreased with the increasing composition of ZnO.

Keywords: glass ZnO-MgO-P2O5; photoluminescence spectrum; melt quenching; XRD; hardness test.

Published
2016-10-30
How to Cite
Budiyanto, E., Budi, A. S., Handoko, E., & Sahar, M. R. (2016). SIFAT MEKANIK DAN OPTIK KACA SENG MAGNESIUM FOSFAT. PROSIDING SEMINAR NASIONAL FISIKA (E-JOURNAL), 5, SNF2016-MPS. https://doi.org/10.21009/0305020222