PENGARUH VARIASI KONSENTRASI SODIUM DODECYL SULFATE (C12H25NaSO4) TERHADAP MORFOLOGI PERMUKAAN PADA PEMBENTUKAN LAPISAN TIPIS KOMPOSIT Ni-TiAlN DENGAN METODE ELEKTRODEPOSISI

Authors

  • Yulia Ermadiana Prodi Fisika FMIPA UNJ, Jl. Pemuda No 10, Jakarta Timur, 13220
  • Esmar Budi Prodi Fisika FMIPA UNJ, Jl. Pemuda No 10, Jakarta Timur, 13220
  • Iwan Sugihartono Prodi Fisika FMIPA UNJ, Jl. Pemuda No 10, Jakarta Timur, 13220

DOI:

https://doi.org/10.21009/03.SNF2017.02.MPS.01

Abstract

Has been done a coating process of the thin composite Ni-TiAlN to review the effect of variations concentration  Sodium Dodecyl Sulfate (C12H25NaSO4) on the surface morphology of thin layer composite Ni-TiAlN. This coating process was using electrodeposition method with a current 0.45μA, voltage 45mV for 15 minutes. This composite was formed on a Tungsten Carbide substrate with solution composition of the electrolyte which consists of 2 gr/l AlN, 2 gr/l TiN, 0.49 Mol/l H3BO3, 0.17 M NiCl26H2O, 0.38 M NiSO46H2O and Sodium Dodecyl Sulfate (C12H25NaSO4). The variation concentration of Sodium Dodecyl Sulfate (C12H25NaSO4)  that used are 0,2 g/l, 0.4 g/l and 0.6 g/l. This research uses characterization  of Scanning Electron Microscopy (SEM) which showed that the bigger of concentration variation of Sodium Dodecyl Sulfate (C12H25NaSO4) make the surface morphology of thin layers composite Ni-TiAlN formed smoother than lower concentration, the smaller of aggregate and  the crack are seen more clearly.

Downloads

Published

2017-10-30

How to Cite

Ermadiana, Y., Budi, E., & Sugihartono, I. (2017). PENGARUH VARIASI KONSENTRASI SODIUM DODECYL SULFATE (C12H25NaSO4) TERHADAP MORFOLOGI PERMUKAAN PADA PEMBENTUKAN LAPISAN TIPIS KOMPOSIT Ni-TiAlN DENGAN METODE ELEKTRODEPOSISI. PROSIDING SEMINAR NASIONAL FISIKA (E-JOURNAL), 6, SNF2017–MPS. https://doi.org/10.21009/03.SNF2017.02.MPS.01