PEMANFAATAN ABU BONGGOL JAGUNG SEBAGAI BAHAN TAMBAH SEMEN PADA PEMBUATAN BATA RINGAN JENIS CLC
DOI:
https://doi.org/10.21009/jmenara.v16i1.16991Keywords:
celullar lightweight concrete, corn cob ash, SNI 03-2156-1991Abstract
This study aims to determine the use of corn cob ash as an additive to cement in the production of CLC lightweight bricks according to SNI 03-2156-1991 concerning air flow light brick blocks by autoclaving process. The method used is an experiment in accordance with SNI 03-2156-1991 regarding light brick blocks of air flow with autoclaving process. The test object measures 59 × 19 ×10 cm and uses 45 specimens. The results obtained for dimensional testing exceed the required limits of SNI 03-2156-1991. The compressive strength of lightweight bricks is obtained at variations of 0%, 4%, 6%, 8%, and 10% respectively 3.07 N/mm², 3.68 N/mm², 4.54 N/mm², 4.29 N/mm², and 4 N/mm² with the optimum compressive strength value obtained at 6% variation and non-passing variation at 0% variation with a minimum requirement of 3.6 N/mm². The flexural strength of lightweight bricks is obtained at variations of 0%, 4%, 6%, 8%, and 10% respectively 0.27 N/mm², 0.63 N/mm², 0.81 N/mm², 0.65 N/mm², and 0.76 N/mm with optimum flexural strength values obtained at 6% variation and non-qualifying variations at 0% and 4% variations with a minimum requirement of 0.65 N/mm².
References
Raheem, A., 2009, Development of Corn Cob Ash Blended Cement, Construction and Building Materials, 23 (1); 347–352
SNI 03-2156-1991. (1991). Badan Standardisasi Nasional.
SNI 03-3449-1994. (1994). Badan Standardisasi Nasional.
SNI 03-1729-2002. (2002). Badan Standardisasi Nasional.
SNI 03-2847-2002. (2002). Badan Standardisasi Nasional.
Surono, U. B. (2010). Peningkatan Kualitas Pembakaran Biomassa Limbah Tongkol Jagung sebagai Bahan Bakar Alternatif dengan Proses Karbonisasi dan Pembriketan Untoro. 4(1), 13–18.
Tjokrodimuljo, K. (1996). Teknologi beton. Nafiri, Yogyakarta.
Tansajaya, A. (2008). Studi pembuatan cellular lightweight concrete (CLC) dengan menggunakan beberapa foaming agent. Petra Christian University.
Velmurugan, P., Shim, J., Lee, K.J., Cho, M., Lim , S. S., Seo, S. K., Cho, K. M., K. Bang , S., Oh, B. T., 2015, Extraction, Characterization, and Catalytic Potential of Amorphous Silica from Corn Cobs by Sol-Gel Method, J. Ind. Eng. Chem, 29 (25); 298-303
Downloads
Published
Issue
Section
License
Authors who publish with this Journal agree to the following terms:
- Author retain copyright and grant the journal right of first publication with the work simultaneously licensed under a creative commons attribution licensethat allow others to share the work within an acknowledgement of the work’s authorship and initial publication of this journal.
- Authors are able to enter into separate, additional contractual arrangementfor the non-exclusive distribution of the journal’s published version of the work (e.g. acknowledgement of its initial publication in this journal).
- Authors are permitted and encouraged to post their work online(e.g. in institutional repositories or on their websites) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published works.