FENOMENA KEKERASAN, IMPAK, DAN STRUKTUR MIKRO BAJA 0.074 wt.% KARBON PASCA QUENCHING COOLANT
Hardness, Impact, and Microstructure Phenomenon of 0.074 C Wt.% Carbon Steel After Quenching in Coolant Liquid
DOI:
https://doi.org/10.21009/JKEM.7.1.5Keywords:
Steel, Quenching, Vickers, Charpy, MicrostructureAbstract
In this research the process of heating the steel material with a carbon content of 0.074 wt % to a temperature of 1000°C. The steel is subject to variations in holding time in the furnace for 10, 20, and 30 minutes. Then various steel that has been held at furnace quenched with coolant media. After quenching, the hardness is measured using the Vickers hardness test and tested with Charphy's impact to know the value of energy absorption. After mechanical testing, everything was finished then proceeds with the optical microscope. The longest holding time affected decreases the hardness and, the impact value will increase. Hardness and impact value are inversely proportional to the variation of holding time that has been done. The specimens formed are ferrite and pearlite based on microstructure observation.
References
[1] A. Alwarits, D. Daswarman, and M. Nasir, “Pengaruh Media Pendingin Pada Proses Hardening Terhadap Peningkatan Kekerasan Baja Karbon Sedang”, Automotive Engineering Education Journals, vol. 2, no. 2, 2014.
[2] A. A. Karim, and Z. A. Yusuf, “Analisa pengaruh penambahan inhibitor kalsium karbonat dan tapioka terhadap tingkat laju korosi pada pelat baja tangki ballast air laut”, J. Ris. dan Teknol. Kelaut, vol. 10, no. 2, pp. 205-212, 2012.
[3] S. Subagiyo, “Analisis Hasil Kekerasan Metode Vikers Dengan Variasi Gaya Pembebanan Pada Baja”, Majapahit Techno: Jurnal Ilmiah dan Teknologi, vol. 6, no. 2, pp. 09-14, 2017.
[4] A. Murtiono, “Pengaruh quenching dan tempering terhadap kekerasan dan kekuatan tarik serta struktur mikro baja karbon sedang untuk mata pisau pemanen sawit”, e-Dinamis, vol. 2, no.2, 2012.
[5] F. B. Susetyo, A. Dudung, S. Wiganda, A. Haris, and W. Nugroho, “Pengaruh Bentuk Kampuh Terhadap Karakteristik Baja Karbon Rendah Hasil Pengelasan SMAW”, Jurnal Konversi Energi dan Manufaktur UNJ, vol. 2, no. 2, pp. 59-64, 2015.
[6] S. Sopiyan, and F. B. Susetyo, “Pengaruh Besar Sudut Kampuh terhadap Kekuatan Tarik Hasil Pengelasan GMAW”, Jurnal Kajian Teknik Mesin, vol. 2 no. 2, pp. 99-105, 2017.
[7] B. H. Setiamarga, N. Kurniawati, and U. Rumendi, “Pack carburizing pada sprocket sepeda motor dengan material baja karbon rendah”, Mesin, vol. 21 no. 1, pp. 28-33, 2017.
[8] H. Hafni, “Pengaruh Waktu Tahan Proses Pack Carburizing Pada Baja Karbon Rendah Dengan Menggunakan Calcium Carbonat Dan Arang Tempurung Kelapa, Di Tinjau Dari Kekerasan”, Jurnal Teknik Mesin (JTM), vol. 5, no. 2, 2015.
[9] H. Purwanto, “Analisa Quenching Pada Baja Karbon Rendah Dengan Media Solar”, Jurnal Ilmiah Momentum, vol. 7. no. 1, 2011.
[10] S. Nugroho, and G. D. Haryadi, “Pengaruh Media Quenching Air Tersirkulasi (Circulated Water) Terhadap Struktur Mikro dan Kekerasan Pada Baja AISI 1045”, Rotasi, vol. 7, no.1, pp. 19-23, 2005.
[11] D. Panuh, D.Yulianto, H. A. Rahman, and N. A. Baharuddin, “Peningkatan Ketangguhan Impact Pisau Mesin Pemotong Rumput Dengan Cara Perlakuan Panas Menggunakan Media Pendingin Coolant Radiator Dan Udara”, Journal of Renewable Energy & Mechanics (REM), vol. 2 no. 01, 2019.
[12] R. Adawiyah, M. Murdjani, and A. Hendrawan, “Pengaruh Perbedaan Media Pendingin Terhadap Struktur mikro dan Kekerasan Pegas Daun Dalam Proses Hardening”, Jurnal Poros Teknik, vol. 6, no. 2, pp. 96-102, 2014.
[13] B. E. Kurniawan, and Y. Setiyorini, “Pengaruh variasi Holding Time Pada Perlakuan Panas Quench Annealing Terhadap Sifat mekanik dan Mikro Struktur Pada Baja mangan AISI 3401”, Jurnal Teknik ITS, vol. 3 no.1, pp. F113-F16, 2014.
[14] S.T. Dwiyati, M.B.P. Hutomo, & F. B. Susetyo, “Pengaruh Variasi Holding Time Dan Media Quenching Terhadap Nilai Kekerasan Baja Dengan Kadar Karbon 0,192Wt.%”. Jurnal Konversi Energi dan Manufaktur UNJ, vol. 6, no. 1, pp. 37-43, 2019.
[15] R. N. Maret, S. Syaripuddin, and F. B. Susetyo, “Pengaruh Kecepatan Pengelasan MIG Pada Pipa SC-80 Terhadap Struktur Mikro Dan Kekerasan Dengan Posisi Pengelasan 1G”, Jurnal Kajian Teknik Mesin, vol. 4, no.2, pp. 76-80, 2019.
[2] A. A. Karim, and Z. A. Yusuf, “Analisa pengaruh penambahan inhibitor kalsium karbonat dan tapioka terhadap tingkat laju korosi pada pelat baja tangki ballast air laut”, J. Ris. dan Teknol. Kelaut, vol. 10, no. 2, pp. 205-212, 2012.
[3] S. Subagiyo, “Analisis Hasil Kekerasan Metode Vikers Dengan Variasi Gaya Pembebanan Pada Baja”, Majapahit Techno: Jurnal Ilmiah dan Teknologi, vol. 6, no. 2, pp. 09-14, 2017.
[4] A. Murtiono, “Pengaruh quenching dan tempering terhadap kekerasan dan kekuatan tarik serta struktur mikro baja karbon sedang untuk mata pisau pemanen sawit”, e-Dinamis, vol. 2, no.2, 2012.
[5] F. B. Susetyo, A. Dudung, S. Wiganda, A. Haris, and W. Nugroho, “Pengaruh Bentuk Kampuh Terhadap Karakteristik Baja Karbon Rendah Hasil Pengelasan SMAW”, Jurnal Konversi Energi dan Manufaktur UNJ, vol. 2, no. 2, pp. 59-64, 2015.
[6] S. Sopiyan, and F. B. Susetyo, “Pengaruh Besar Sudut Kampuh terhadap Kekuatan Tarik Hasil Pengelasan GMAW”, Jurnal Kajian Teknik Mesin, vol. 2 no. 2, pp. 99-105, 2017.
[7] B. H. Setiamarga, N. Kurniawati, and U. Rumendi, “Pack carburizing pada sprocket sepeda motor dengan material baja karbon rendah”, Mesin, vol. 21 no. 1, pp. 28-33, 2017.
[8] H. Hafni, “Pengaruh Waktu Tahan Proses Pack Carburizing Pada Baja Karbon Rendah Dengan Menggunakan Calcium Carbonat Dan Arang Tempurung Kelapa, Di Tinjau Dari Kekerasan”, Jurnal Teknik Mesin (JTM), vol. 5, no. 2, 2015.
[9] H. Purwanto, “Analisa Quenching Pada Baja Karbon Rendah Dengan Media Solar”, Jurnal Ilmiah Momentum, vol. 7. no. 1, 2011.
[10] S. Nugroho, and G. D. Haryadi, “Pengaruh Media Quenching Air Tersirkulasi (Circulated Water) Terhadap Struktur Mikro dan Kekerasan Pada Baja AISI 1045”, Rotasi, vol. 7, no.1, pp. 19-23, 2005.
[11] D. Panuh, D.Yulianto, H. A. Rahman, and N. A. Baharuddin, “Peningkatan Ketangguhan Impact Pisau Mesin Pemotong Rumput Dengan Cara Perlakuan Panas Menggunakan Media Pendingin Coolant Radiator Dan Udara”, Journal of Renewable Energy & Mechanics (REM), vol. 2 no. 01, 2019.
[12] R. Adawiyah, M. Murdjani, and A. Hendrawan, “Pengaruh Perbedaan Media Pendingin Terhadap Struktur mikro dan Kekerasan Pegas Daun Dalam Proses Hardening”, Jurnal Poros Teknik, vol. 6, no. 2, pp. 96-102, 2014.
[13] B. E. Kurniawan, and Y. Setiyorini, “Pengaruh variasi Holding Time Pada Perlakuan Panas Quench Annealing Terhadap Sifat mekanik dan Mikro Struktur Pada Baja mangan AISI 3401”, Jurnal Teknik ITS, vol. 3 no.1, pp. F113-F16, 2014.
[14] S.T. Dwiyati, M.B.P. Hutomo, & F. B. Susetyo, “Pengaruh Variasi Holding Time Dan Media Quenching Terhadap Nilai Kekerasan Baja Dengan Kadar Karbon 0,192Wt.%”. Jurnal Konversi Energi dan Manufaktur UNJ, vol. 6, no. 1, pp. 37-43, 2019.
[15] R. N. Maret, S. Syaripuddin, and F. B. Susetyo, “Pengaruh Kecepatan Pengelasan MIG Pada Pipa SC-80 Terhadap Struktur Mikro Dan Kekerasan Dengan Posisi Pengelasan 1G”, Jurnal Kajian Teknik Mesin, vol. 4, no.2, pp. 76-80, 2019.
Downloads
Published
2022-01-15
How to Cite
[1]
Basori and A. Iswadi, “FENOMENA KEKERASAN, IMPAK, DAN STRUKTUR MIKRO BAJA 0.074 wt.% KARBON PASCA QUENCHING COOLANT: Hardness, Impact, and Microstructure Phenomenon of 0.074 C Wt.% Carbon Steel After Quenching in Coolant Liquid”, J. Konversi Energi dan Manufaktur, vol. 7, no. 1, pp. 35–41, Jan. 2022.
Issue
Section
Articles