THE UTILIZATION OF CONCRETE WASTE AS AN AGGREGATE SUBSTITUTE AND THE ADDITION OF DENIM FABRIC FIBERS ON COMPRESSIVE AND FLEXURAL STRENGTH OF CONCRETE : (AS AN IMPLEMENTATION OF CONCRETE TECHNOLOGY COURSE)

Farid Muhamad Harahap; Anisah Anisah; Ririt Aprilin

doi:10.21009/jpensil.v14i2.53724

Authors

Farid Muhamad Harahap State University of Jakarta
Anisah Anisah
Ririt Aprilin

DOI:

https://doi.org/10.21009/jpensil.v14i2.53724

Keywords:

Compressive Strength, Fiber Concrete, Flexural Strength, Denim Fabric, Waste Concrete

Abstract

Concrete is one of the construction materials used in building structures, bridges, roads, and others. The material components that make up concrete consist of fine aggregates (sand), coarse aggregates (gravel), water, and cement. However, the drawbacks of concrete include low tensile strength, heavy weight, high sound reflection, and difficulty in reshaping after it has been formed. Adding fibers is one way to increase the flexural strength of concrete. This study aims to determine the utilization of concrete waste and the addition of denim fabric fibers in improving the compressive strength and flexural strength of concrete, using fiber lengths of 100 mm and widths of 5 mm with variations of fiber addition at 1% and 2%. The test results at 28 days show the compressive strength values of control concrete, concrete with 1% fiber proportion, and 2% fiber proportion are 10,27 MPa, 8,3 MPa, and 5,44 MPa, respectively, with the optimum compressive strength being 10,27 MPa for the control concrete. Therefore, none of the compressive strengths reached the design compressive strength of 40 MPa. The flexural strength values from the tests are 3,52 MPa, 4,32 MPa, and 2,98 MPa, with the optimum flexural strength being 4,32 MPa at the 1% fiber proportion. The flexural strength values range between 34,27% to 54,77% of the compressive strength values.

References

Ahmad, A., Jasman, J., & Hamsyah, H. (2024). Pengaruh Penambahan Serat Ijuk dan Plasticezer Sebagai Bahan Tambah Terhadap Nilai Karakteristik Beton. Jurnal Publikasi Rumpun Ilmu Teknik , 2(2), 55–62.

Amna, K., Wesli, & Hamzani. (2017). Pengaruh Penambahan Serat Tandan Sawit Terhadap Kuat Tekan Dan Kuat Lentur Beton. Teras Jurnal : Jurnal Teknik Sipil, 4(2), 11–20. https://doi.org/10.29103/tj.v4i2.19

Andika, Y., Scorle, N., & Rehi, B. (2021). Pengaruh Waktu Pencampuran Terhadap Kuat Tekan Beton Dengan Bahan Tambah Sikament®-LN. Jurnal Karkasa, 6(1).

Catur, A. D., Setyawan, P. D., Padang, Y. A., Nuarsa, I. M., & Triadi, A. A. A. (2022). Kuat Lentur dan Berat Jenis Beton Ringan Selular Diperkuat Serat Kain Pakaian Bekas. Dinamika Teknik Mesin, 12(1), 8. https://doi.org/10.29303/dtm.v12i1.497

Candra, 8Agata Iwan, Gardjito, E., Cahyo, Y., & Prasetyo, G. A. (2019). Pemanfaatan Limbah Puntung Rokok Filter Sebagai Bahan Campuran Beton Ringan Berpori. UKaRsT, 3(1), 82. https://doi.org/10.30737/ukarst.v3i1.365

Dian Hardiyanti, A., Hayati, Y., & Abbas, I. (2022). Sifat Mekanis Beton Busa dengan Serat. Universitas Syiah Kuala Jalan Syech Abdurrauf, 23111(7).

Dumiyati, A., & Manalu, doni fransiskus. (2015). Analisis Penggunaan Pasir Pantai Paciran Sebagai Agregat Halus Terhadap Kuat Tekan Beton. DEARSIP : Journal of Architecture and Civil, 2(1), 8–17. https://doi.org/10.52166/dearsip.v2i1.3352

Fahruroji, R., Marlina, R., & Widiana, I. (2020a). Kajian Karakteristik Geotekstil Dari Limbah Kain Denim (Study Of Geotextile Characteristics From Denim Fabric Waste).

Fahruroji, R., Marlina, R., & Widiana, I. (2020b). Kajian Karakteristik Geotekstil Dari Limbah Kain Denim Study of Geotextile Characteristics From Denim Fabric Waste. 390, 113–120.

Febby Romaadhoni, S., Ridwan, A., Winarto, S., & Candra, A. I. (2019). Studi Experimen Kuat Tekan Beton Dengan Memanfaatkan Limbah Keramik Dan Bata Merah. Jurnal Manajemen Teknologi & Teknik Sipil, 2(1), 86. https://doi.org/10.30737/jurmateks.v2i1.394

Firda, A., Permatasari, R., & Syahrul Fuad, I. (2021). Pemanfaatan Limbah Batu Bara (Fly Ash) Sebagai Material Pengganti Agregat Kasar Pada Pembuatan Beton Ringan (Vol. 6, Issue 1).

Hani, S. (2018). PENGARUH CAMPURAN SERAT PISANG TERHADAP BETON. Universitas Pembinaan Masyarakat Indonesia, 4.

Haryanto, Y. (2016). Pengaruh Serat Limbah Karpet Terhadap Kuat Lentur Balok Beton Ringan dari ALWA. Effect of Carpet Waste Fiber to The Flexural Strength of ALWA Lightweight Concrete Beams (Vol. 17, Issue 2).

Irawan, D., & Khatulistiani, U. (2021). Substitusi Agregat Kasar Menggunakan Pecahan Tempurung Kelapa Pada Campuran Beton Normal. Axial : Jurnal Rekayasa Dan Manajemen Konstruksi, 9(1), 061. https://doi.org/10.30742/axial.v9i1.1703

Ishaq, M., Nasmirayanti, R., Yuda Trinanda, A., kunci, K., Tekan, K., Beton, L., & Rencana, U. (2021). Pengaruh Limbah Pecahan Beton Sebagai Pengganti Agregat Kasar Terhadap Kuat Tekan Beton. 6(2). https://doi.org/10.35134/jcivil.v3i2.001-006

Kartini, W. (2019). Penggunaan serat polypropylene untuk meningkatkan kuat tarik belah beton. Rekayasa Perencanaan, 4(1), 1–13.

Kholis, I. N., Sat, D., Yuwana, A., & Susilowati, F. (2022). Penambahan Serat Kain Limbah Konveksi dan Pecahan Kaca Sebagai Bahan Tambah Agregat Halus Terhadap Kuat Tekan dan Kuat Lentur Beton.

Khonado, M. fransisca, Manalip, H., & Wallah, steenie e. (2019). Kuat Tekan Dan Permeabilitas Beton Porous Dengan Variasi Ukuran Agregat. Jurnal Sipil Statik, 7 No. 3(3), 351–358.

Klau, A. S., Phengkarsa, F., & Sanggaria ’, O. J. (2021). Pemanfaatan Limbah Cangkang Telur Sebagai Bahan Substitusi Semen Pada Beton.

Lee, S. (2019). Effect of nylon fiber addition on the performance of recycled aggregate concrete. Applied Sciences (Switzerland), 9(4). https://doi.org/10.3390/app9040767

Lestari, D. D. (2022). Pengaruh Variasi Campuran Serat Bambu Pada Kuat Tekan Beton Serat. Dinamika Teknik Sipil: Majalah Ilmiah Teknik Sipil, 1(1), 1–7. https://doi.org/10.23917/dts.v1i1.17027

Lubis, K., & Hermanto, E. (2020). Pembuatan Genteng Beton Serat Dengan Bahan Tambah Serat Serabut Kelapa Dan Styrofoam. Cetak) Buletin Utama Teknik, 15(2), 1410–4520.

Megasari, S. W., Yanti, G., & Zainuri. (2016). Karakteristik Beton dengan Penambahan Limbah Serat Nylon dan Polimer Concrete. Jurnal Teknik Sipil Siklus, 1, 25–34.

Patti, A., Cicala, G., & Acierno, D. (2020). polymers Eco-Sustainability of the Textile Production: Waste Recovery and Current Recycling in the Composites World. https://doi.org/10.3390/polym1301

Periyasamy, A. P., & Periyasami, S. (2023). Critical Review on Sustainability in Denim: A Step toward Sustainable Production and Consumption of Denim. ACS Omega Publications, 8, 4472–4490.

Permata, A. R., Cory, M., Siagian, A., Ds, S., & Sn, M. (2021). Pengolahan Limbah Denim Menggunakan Eksplorasi Teknik Surface Textile Design Pada Produk Fesyen.

Permatasari, S. (2019). Pengaruh Bahan Tambah Batu Bata Merah Terhadap Kuat Tekan Beton Fc ’ 21 Menggunakan Agregat Kasar Pt . Amr Dan Agregat Halus Desa Sunggup Kota Baru. Jurnal Tapak, 8(2), 155–161.

Prahara, E., Liong, G. T., & Rachmansyah. (2015). Analisa Pengaruh Penggunaan Serat Serabut Kelapa dalam Presentase Tertentu pada Beton Mutu Tinggi. ComTech: Computer, Mathematics and Engineering Applications, 6(2), 208. https://doi.org/10.21512/comtech.v6i2.2265

Prasanti, P. P., & Saelan, P. (2019). Tinjauan Kembali Mengenai Batasan Gradasi Agregat Kasar dalam Campuran Beton. (Hal. 118-125). RekaRacana: Jurnal Teknil Sipil, 5(3), 118. https://doi.org/10.26760/rekaracana.v5i3.118

Sahrudin, & Nadia. (2016). Pengaruh Penambahan Serat Sabut Kelapa terhadap Kuat Tekan beton. Pengaruh Penambahan Serat Sabut Kelapa Terhadap Kuat Tekan Beton, 13–20.

Suhendra, rara amelia, & Amalia, kiki rizky. (2021). Hubungan Faktor-Faktor yang Mempengaruhi Kuat Tekan Beton. Jurnal Talenta Sipil, 4(2), 225. https://doi.org/10.33087/talentasipil.v4i2.79

Sulianti, I. A. S. R. D. (2018). Analisis Pengaruh Besar Butiran Agregat Kasar Terhadap Kuat Tekan Beton Normal. Analisis Pengaruh Besar Butiran Agregat Kasar Terhadap Kuat Tekan Beton Normal, 7(1), 35–42.

Tran, N. P., Gunasekara, C., Law, D. W., Houshyar, S., Setunge, S., & Cwirzen, A. (2022). Comprehensive Review on Sustainable Fiber Reinforced Concrete Incorporating Recycled Textile Waste. Journal of Sustainable Cement-Based Materials, 11(1), 41–61. https://doi.org/10.1080/21650373.2021.1875273

Trimurtiningrum, R. (2018). Pengaruh Penambahan Serat Bambu Terhadap Kuat Tarik dan Kuat Tekan Beton. Jurnal Hasil Penelitian LPPM Untag Surabaya Januari, 03(01), 1–6.

Vitri, G., & Herman, H. (2019). Pemanfaatan Limbah Kelapa Sawit Sebagai Material Tambahan Beton. Jurnal Teknik Sipil ITP, 6(2), 78–87. https://doi.org/10.21063/jts.2019.v602.06

Widiarini, M. R. (2023). Pengaruh Penambahan Limbah Plastik Botol Air Mineral Terhadap Kuat Tekan, Kuat Tarik dan Kuat Lentur Beton (The Effect Of Adding Mineral Water Plastic Waste On The Compressive Strength, Tensile Strength, And Flexural Strength Of Concrete).

Widodo, A. (2012). Pengaruh Penggunaan Potongan Kawat Bendrat Pada Campuran Beton Dengan Konsentrasi Serat Panjang 4 Cm Berat Semen 350 Kg/M 3 Dan Fas 0,5. Jurnal Teknik Sipil & Perencanaan, 14(2), 131–140.

Winarno, E. (2021). Analisa subtitusi limbah karbit serta penambahan serat limbah kain pada kuat tekan beton. 11(3), 1–14.

Wora, M., & Ndale, F. X. (2018). Pengaruh Penambahan Serat Ijuk Dapat Meningkatkan Kuat Tarik pada Beton Mutu Normal. Jurnal IPTEK, 22, 51–58. https://doi.org/10.31284/j.iptek.2018.v22i2

Zakirah, R., Abdullah, & Amalia, Z. (2023). Penggunaan Agregat Kasar dari Limbah Beton terhadap Kekuatan Beton. Journal of The Civil Engineering Student, 5, 337–343.

Zalukhu, P. S., Irwan, & Hutauruk, D. M. (2017). Pengaruh Penambahan Serat Sabut Kelapa (Cocofiber) terhadap Campuran Beton sebagai Peredam Suara. Journal of Civil Engineering, Building and Transportation, 1(1), 27. https://doi.org/10.31289/jcebt.v1i1.367

Zuraidah, S., Hastoro, K. budi, & Jehabut, M. A. (2022). Pemanfaatan Limbah Cangkang Kemiri Sebagai Substitusi Agregat Kasar Pada Beton. Jurnal Perencanaan Dan Rekayasa Sipil, 5(2), 93–98.